LoTherme-703

Low heat input electrode for high-strength machinable deposit. Highly suitable for crack-free joining of Cast Iron to Steel.

Characteristics

LoTherme-703 produces high strength, machinable welds and overlays on grey and alloy cast irons. Deposits are even crack-free on joints of Cast Iron to Steels. A stable arc and evenly rippled, smooth beads are some of the many pleasant features of the electrode.

Applications

LoTherme-703 is used for :

1. Welding grey cast iron, malleable iron and S.G. iron ;

2. Welding cast iron to steel and to nickel alloys and ;

3. Repair welds and rectification of defects in castings.                                                                       

Typical applications include engine heads, pump castings, impellers, rope drums, ingot moulds and a variety of cast iron machine parts. Due to the high strength and ductility, LoTherme-703 is ideal for welding heavy and highly stressed cast iron sections.

Typical Mechanical Properties Of All Weld Metal

ULTIMATE TENSILE STRENGTH : 43 Kgf/mm2

HARDNESS : 190 BHN

Welding Technique

For joining bevel the edges to 75-90° in single or double 'Vee' groove according to thickness of the parts. For repair of cracks, drill holes at the two ends of the crack to arrest its further propagation. Remove entire cracked material to sound metal by chipping, gouging or machining. Clean the weld area free of grease, oil, paints, etc. prior to welding. Weld short beads not exceeding 50 mm at a time. Each bead should be peened when still hot. For large and heavy sections pre heating of the job may be necessary. After the welding is completed, the castings should be covered completely with a layer of asbestos or dry lime until it attains room temperature.

Current Conditions : AC/DC (-)


Size (mm)
5x350
4x350
3.15x350
2.5x350
Current Range (Amps)
130-170
100-130
85-120
50-70