Rail Crossing

Industry Type
Steel Foundry

Product Group
Lotherme

OUR SOLUTION

Problem
Pin & Blow Hole

Dimensions & Weight
L-5500 mm xT- 225 mm x W-450 mm & WT- 1080 kgs

Previous Solution
Ok 13MN (esab)

Our Product Used
L-607

Size (mm)
4.00

Quantity (Kgs)
½ kgs approx

JOB PICTURES

Job Pic Before Repair

Job Pic Before Repair

Job Pic After Repair

Job Pic After Repair

ANALYSIS

Equipment Name
Crossing

Base Metal
Mn Steel

Wear Factor
Buildup finishing

Procedure

Dry electrodes at 2500C for one hour. clean the weld area very well by gauging, grinding and cleaning agent after that DP test done due to fully remove the crack from the metal, then use our L-607 with low current ,shot arc and stringer beads for joining or resurfacing of austenitic mn steel.