BATOX-F(U) - E316L-15 (Modified)
DOWNLOAD SPECS
DOWNLOAD SPECS

Stainless Steel Electrodes

BATOX-F(U)

AWS: SFA 5.4 E316L-15 (Modified)

Batox-F(U) is a semi-basic coated electrode depositing a weld metal which is fully austenitic in structure, has high strength and good crack resistance. The weld metal displays remarkable corrosion resistance particularly in urea service. Ideally suitable for welding of AISI 316L and their nitrogen bearing versions particularly for urea service.

Precaution

1. Ensure the electrodes are dry. Re-dry the electrodes at 250-300°C for one hour.

2. Use short arc, stringer bead, smallest size of electrode and minimum current to ensure minimum heat input.

CHEMICAL COMPOSITION OF ALL WELD METAL (%)


Element
CMnSiCrNiNMoSP
Percent
0.034.00.4519.516.00.152.80.0150.020

FERRITE CONTENT : Nil

MECHANICAL PROPERTIES OF ALL WELD METAL


UTSElongation
Corrosion Rate
(MPa)
(L= 4d)%
(ASTM A262 Practice C)
63437.07 mils/year



CURRENT AND PACKING DATA: AC / DC(+)


Size (mm)
5x3504x350
3.15x350
2.5x350
Current Range (Amps)
150-180110-140
80-100
60-80
Weight / Carton (kgs)
2.52.5
2.5
2.5