MAXFLUX SAF -223 -F7A4EH-14, F7A4EM-12K, F8A2EA2-A2
DOWNLOAD SPECS
DOWNLOAD SPECS

Flux

MAXFLUX SAF -223

AWS: SFA 5.17/5.23 F7A4EH-14, F7A4EM-12K, F8A2EA2-A2

Maxflux SAF-223 is an agglomerated basic type flux for high-speed longitudinal welding giving smooth & shiny weld bead along with easy slag removal characteristics. The flux is also suitable for multi-wire submerged arc welding applications and supports to achieve higher throat thickness in welding of fillet joints due to higher current carrying capacity.

Maxflux SAF-223 is suitable for single & multi-layer welding of pressure vessel grade steels (EN 10028-2), X-42 to X-70 grade pipes conforming to API-5L specification, etc. 

Precaution

Re-dry the flux at 300-350 C for two hours before use.

CHEMICAL COMPOSITION OF ALL WELD METAL (%)


WITH SAW WIRE
Elements
CMnSiSPMoCu
AUTOTHERME GRADE-B
Typical
0.070 
1.00 0.25 0.022 0.025 - 0.15
AUTOTHERME GRADE-C
Typical
0.100 1.40 0.38 0.020 0.023 - 0.15
AUTOTHERME GRADE-F
Typical
0.070 1.38 0.59 0.018 0.022 0.47 0.15

    

MECHANICAL PROPERTIES OF ALL WELD METAL


WITH SAW WIRE
UTS 
0.2% YS % EI CVN Impact (Joules)
 CVN Impact (Joules)
 CVN Impact (Joules)
CVN Impact (Joules)

(Mpa)
(Mpa)
(L=4d)
 -20°C
-29°C-40°C
-46°C

AUTOTHERME GRADE-B

 510 440 30 - 78 45-

AUTOTHERME GRADE-C

 580 505 28 - 80 50
-
AUTOTHERME GRADE-F
 620 530 27 60 85
--

    

MAJOR CONSTITUTENTS


SiO2 + TiO2 CaO+MgO Al2O3+MnO CaF2
10%
40%
30%
20%

    

Additional Information

BASICITY INDEX : ~1.60

GRAIN SIZE : 0.20 – 1.50 mm

PACKAGING : 25 Kg POLY-LINED PAPER BAG