SAW Flux MAXFLUX SAF -223 (MOD) - F7A5-EH14, F7A5-EM12K, F8A4-EA2-A2
DOWNLOAD SPECS
DOWNLOAD SPECS

Flux

MAXFLUX SAF-223 (MOD)

AWS: SFA 5.17/5.23 F7A5-EH14, F7A5-EM12K, F8A4-EA2-A2

Maxflux SAF-223 (Mod) is an agglomerated basic type flux for high speed welding of longitudinal pipe giving smooth & shiny weld bead with improved impact toughness properties. The flux is also suitable for multi-wire submerged arc welding applications and supports to achieve higher throat thickness in welding of fillet joints due to higher current carrying capacity.

Maxflux SAF-223 (Mod) is suitable for single & multi-layer welding of pressure vessel grade steels (EN 10028-2), X-42 to X-70 grade pipes conforming to API-5L specification, etc.

Precaution

Re-dry the flux at 300-350°C for two hours before use.

CHEMICAL COMPOSITION OF ALL WELD METAL (%)


WITH SAW WIRE
Elements
CMnSiSPMo
AUTOTHERME GRADE-B
Typical
0.065 
1.55 0.52 0.017 0.025-
AUTOTHERME GRADE-C
Typical
0.100 1.40 0.38 0.020 0.023-
AUTOTHERME GRADE-F
Typical
0.070 
1.31 0.59 0.018 0.022   0.470  
MECHANICAL PROPERTIES OF ALL WELD METAL


WITH SAW WIRE
UTS 
0.2% YS % EI CVN Impact (Joules)
 CVN Impact (Joules)
 CVN Impact (Joules)

(MPa)
(MPa)
(L=4d)
 -29°C
-40°C-46°C

AUTOTHERME GRADE-B

550 
455 27--60

AUTOTHERME GRADE-C

572 460 26 80 60 40

AUTOTHERME GRADE-F

630 570 25 50 40-

    

MAJOR CONSTITUTENTS


SiO2 + TiO2 CaO + MgO Al2O3 + MnO CaF2
10%
40%
30%
20%

    

Additional Information

BASICITY INDEX: ~1.60

GRAIN SIZE: 0.20 – 1.50 mm

PACKAGING: 25 Kg POLY-LINED PAPER BAG