A low hydrogen electrode yielding a tough and ductile weld deposit having 1% Ni- 0.25% Mo suitable for welding fine-grained and Ni steels for service temperatures down to minus 60°C. Typical applications include storage tanks for liquefied gases, distillers in coke oven batteries and petrochemical industries. Ideal for welding high strength and fine-grained steels subjected to sever dynamic loading and sub-zero temperature service.
Element | C | Mn | Si | Ni | Mo | S | P |
Percent | 0.06 | 0.90 | 0.30 | 0.90 | 0.25 | 0.020 | 0.020 |
UTS | YS | Elongation | CVN Impact Strength (J) |
(MPa) | (MPa) | (L= 4d)% | at Minus 40°C |
574 | 505 | 27.0 | 50 |
Size (mm) | 5x350 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 210-270 | 150-190 | 100-135 | 80-100 |
Qty. (Pcs./Carton) | 35 | 55 | 75 | 125 |
E8016-C2
E8018-C4
E7018-1
E8018-C3
E8018-G
E8018-G H4R
E7018-C1L
E8018-NM1
E7018-1
E8018-G
E8018-C1
E8016-C1
E10018-G
E7018-G
E7018-1H4R
E7018-C3L
E8018-G
E8018-C2
E7018-C2L
E7018-1H4R
E7016-C2L