D&H 2209(NS) - E2209-16
DOWNLOAD SPECS
DOWNLOAD SPECS

Stainless Steel Electrodes

D&H 2209(NS)

AWS: SFA 5.4 E2209-16 EN ISO CODE: 3581-A E 22 9 3 N L R 3 2

D&H 2209(NS) is a non-synthetic electrode depositing duplex stainless steel weld metal. It is ideal for welding duplex stainless steels. The weld metal possesses excellent corrosion resistance in marine & paper environments. Suitable for welding duplex stainless steels having Cr < 25% and other grades like UNS 32205, UNS 31803, etc.

Precaution

1. Ensure the electrodes are dry. Re-dry the electrodes at 250-300°C for one hour.

2. Use stringer beads, short arc and smallest possible size, which helps in reducing the heat input.


Note : D&H 2209-15 (NS) conforming to AWS E2209-15 is also available.

Approvals
    CE
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL


Element
CMnSiPSCrNiMoN
Percent
0.0281.50.40.0200.01822.58.83.00.14


TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL


UTSYS
Elongation
CVN Impact (J)
Hardness
(MPa)
(MPa)
(L= 5d)%
at Minus 30°C
(RC)
7235502570
24



CURRENT AND PACKING DATA: AC / DC(+)


Size (mm)

Dia x Length

5x3504x350
3.15x350
2.5x350
Current Range (Amps)
150-180110-140
80-110
60-80
Weight / Carton (kgs)
2.52.5
2.5
2.5


CORROSION PROPERTY

Weld metal meets ASTM A262 Practice C, ASTM G-36, ASTM G-48A and NACE TM-01-77 specification at 350 MPa stress level, 16 bar pressure and 90°C temperature requirements in as welded condition.

FERRITE (FN)

40-55

BEND TEST

Satisfactory with plunger diameter equal to 4 times the thickness of the specimen.