D&H 385 - E385-16
DOWNLOAD SPECS
DOWNLOAD SPECS

Stainless Steel Electrodes

D&H 385

AWS: SFA 5.4 E385-16 EN ISO CODE: 3581-A E 20 25 5 CuNL R 3 2

D&H 385 is a non-synthetic rutile coated stainless steel electrode depositing a weld metal containing low carbon 20Cr - 25Ni - 5Mo - 2Cu which exhibits excellent resistance to corrosion in non oxidizing media like sulfuric acid, phosphoric acid, acetic acid, formic acid, fatty acids, oxalic acid etc.

*Soft and stable arc, which is easy to strike and re-strike. * Low spatter. * Smooth weld beads. * Easy slag detachability.

It is ideally suited for welding materials for application where phosphoric, sulfuric acids, and other non-oxidizing solutions are encountered. The addition of Mo and Cu in the weld metal helps in resisting corrosive attack of these solutions. It is particularly suited for welding Carpenter 20, HV9, HV9A, Uranus B6, UHB 904L, Sandvik 2RK65, and similar materials which are used for these service conditions.

Precaution

1. Ensure the electrodes are dry. Re-dry the electrodes at 250-300 C for one hour.

2. Use stringer beads, short arc and smallest possible size, which helps in reducing the heat input.

Approvals
    CE
CHEMICAL COMPOSITION OF ALL WELD METAL (%)


Element
CMnSiCrNiMoCuSP
Percent
0.0302.00.4020.024.04.41.800.0120.020


MECHANICAL PROPERTIES OF ALL WELD METAL


UTSElongation
(MPa)
(L= 5d)%
54532.0



CURRENT AND PACKING DATA: AC / DC(+)


Size (mm)
5x3504x350
3.15x350
2.5x350
Current Range (Amps)
140-180110-140
80-100
60-80
Weight / Carton (kgs)
2.52.5
2.5
2.5