D&H 1212(MOD) - ENiCrFe-3 (Approx.)
DOWNLOAD SPECS
DOWNLOAD SPECS

Electrodes for Nickel and it's Alloys

D&H 1212(MOD)

AWS: SFA 5.11 ENiCrFe-3 (Approx.) EN ISO CODE: 14172:ENi6082

Electrode is depositing 65Ni-20Cr-2Nb-1.5Mo weld metal. Radiographic quality weld metal of superior properties. It is ideally suited for welding alloys of similar compositions to themselves, for surfacing steel with Nickel-Chromium-Iron alloy when high Manganese contents are not detrimental, for welding clad side of Nickel Chromium-Iron clad steel and dissimilar metal combinations. Suitable for overlay of forge plates. Specially recommended for welding 9% Ni Steels for cryogenic service. Also used for welding of Nickel-Chromium alloys used for high temperature applications like furnace heating elements and reformer tubes.

Precaution

1. Ensure the electrodes are dry. Re-dry the electrodes at 300-325°C for one hour.

2. Maintain a short arc, stringer bead and minimize the heat input.

3. Allow the weld to cool down to below 50°C before depositing, the next layer.

Approvals
    CE
    BHEL
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL


Element
CMnSiCrNiMoFeNbCuTi
Percent
0.044.00.5020.0Bal.1.53.02.00.300.30


TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL


UTSYSElongation
CVN Impact Strength 
Lateral Expansion
Creep Strength 
(MPa)
(MPa)
(L= 5d)%
at Minus 196°C (J)
at minus 196°C (mm)
at 600°C for 1000 hrs.
62050030
75
0.85160 MPa



CURRENT AND PACKING DATA: DC (+)


Size (mm) Dia x Length

5x3504x350
3.15x350
2.5x350
Current Range (Amps)
150-180120-150
80-110
60-70
Weight/Carton (kgs)
2.52.5
2.5
2.5