D&H 1400 nickel electrodes deposits Ni-Cr-Mo-W-Co. The weld deposit has excellent heat resistance and strength up to 1000°C. The deposit work hardens under impact load and the hardness is retained even at elevated temperatures. The weld deposit of nickel electrodes has high resistance to static or cyclic loads at high temperatures. D&H 1400 nickel electrodes are ideally suited for surfacing applications and joining applications to resist corrosion due to chloride environment and for surfacing of hot working tools, dies, punches, etc.
1. Ensure the electrodes are dry. Re-dry the electrodes at 300-325°C for one hour.
2. Use short arc and minimise heat input.
3. Clean the area thoroughly free from all contamination.
4. Wherever possible weld in flat position only.
Element | C | Mn | Si | Cr | Ni | Mo | W | Fe | Co |
Percent | 0.05 | 0.60 | 0.50 | 15.0 | Balance | 15.5 | 3.5 | 5.0 | 2.0 |
UTS | Elongation |
(MPa) | (L= 5d)% |
713 | 28.0 |
Size (mm) Dia x Length | 5x350 | 4x350 | 3.15x350 | 2.5x350 |
Current Range (Amps) | 150-180 | 120-150 | 80-110 | 60-70 |
Weight/Carton (kgs) | 2.5 | 2.5 | 2.5 | 2.5 |